Abstract High electrical conductivity is desired in MXene films for applications such as electromagnetic interference shielding, antennas, and electrodes for electrochemical energy storage and conversion applications. Due to the acid etching-based synthesis method, it is challenging to deconvolute the relative importance that factors such as chemical composition and flake size contribute to resistivity. To understand the intrinsic and extrinsic contributions to the macroscopic electronic transport properties, a systematic study controlling compositional and structural parameters was conducted with eight solid solutions in the Ti y Nb 2− y CT x system. In particular, we investigated the different roles played by metal (M)-site composition, flake size, and d -spacing on macroscopic transport. Hard x-ray photoemission spectroscopy and spectroscopic ellipsometry revealed changes to electronic structure induced by the M-site alloying. Consistent with the spectroscopic results, the low- and room-temperature conductivities and effective carrier mobility are correlated with the Ti content, while the impact of flake size and d -spacing is most prominent in low-temperature transport. The results provide guidance for designing and engineering MXenes with a wide range of conductivities. 

We report the synthesis and characterization of as-grown SrFexMn1-xO2.5 epitaxial films, which were also subjected to post-growth oxidation and topotactic fluorination to obtain SrFexMn1-xO3 and SrFexMn1-xO(2.5-d)Fg films. We show how both the B-site cation and anion composition influence the structural, electronic, and optical properties of this family of perovskite materials. The Fe substitution of Mn in SrMnO2.5 gradually expands the c-axis parameter, as indicated by X-ray diffraction. With increasing x, the F content incorporated under identical fluorination conditions increases, reaching its maximum in SrFeO(2.5-d)Fg. In the compounds with mixed B-site occupation, the Fe 2p photoemission peaks are shifted upon fluorination while the Mn 2p peaks are not, suggesting inductive effects lead to asymmetric responses in how F alters the Mn and Fe bonds. Electronic transport measurements reveal all compounds are insulators, with the exception of SrFeO3, and demonstrate that fluorination increases resistivity for all values of x. Optical absorption spectra in the SrFexMn1-xO2.5 and SrFexMn1-xO3 films evolve systematically as a function of x, consistent with a physical scenario in which optical changes with Fe substitution arise from a linear combination of Mn and Fe 3d bands within the electronic structure. In contrast, the F incorporation induces non-linear changes to the optical response, suggesting a more complex impact on the electronic structure in materials with concurrent B-site and anion site substitution.